Chemické reaktorové cievy: 316ti vs . 904 l pre kyslú službu

 

Prečo sa 316ti bežne používa pre reaktory kyseliny sírovej?
316Ti's titanium stabilization prevents sensitization during welding, making it suitable for 20-80% sulfuric acid at moderate temperatures (up to 60℃). Its molybdenum content (2-3%) provides adequate pitting resistance, while costing 30% less than super austenitic grades.

 

Kedy sa vyžaduje 904L pre agresívnu službu kyseliny?
904L is mandatory for nitric, phosphoric, and mixed acids above 60℃. Its high nickel (24-26%) and molybdenum (4-5%) content resist oxidizing conditions and chlorides. Critical for processes involving hydrofluoric or sulfuric acid contamination.

 

Maximálne teplotné limity pred poruchou?
316ti: Bezpečné až 100 stupňov pri redukcii kyselín, ale zlyhá nad 40 stupňov oxidačného média .
904L: Zvláda vriaci kyselina dusičná (120 stupňov) a 80 stupňov kyseliny sírovej s<0.1 mm/year corrosion.

 

Kritické zváracie opatrenia?
Nízko teploty GTAW so zodpovedajúcimi plniacimi kovmi (ER316ti pre 316ti, ER385 pre 904L) . po zváranom roztoku žíhajúcich sa pri 1100 stupňoch rozpustí škodlivé sekundárne fázy . Ferrite.<5% for 904L).

 

Osvedčené postupy monitorovania korózie?
Mapovanie ultrazvukovej hrúbky každých 6 mesiacov . Elektrochemická impedančná spektroskopia detekuje pasívne rozkladanie filmu {{}} Testovanie kupónov v procesných tekutinách overuje výkon materiálu .